High temperature phosphorus oxide diffusion source

ABSTRACT

The present invention relates to a solid high temperature phosphorus diffusion source that is an R2O3/P2O5 compound in which the ratio of R2O3 to P2O5 is 1 to 3 and R is La, Y, Ce, Nd, Eu, Pt, Sm, Ho, Tb, Er, Yb, Tm or Dy. The invention also relates to a method of making the diffusion source, a method of using the diffusion source to evolve P2O5 to dope a silicon wafer, and to the doped silicon wafer.

The present invention relates to a solid high temperature phosphorus diffusion source that is an R₂ O₃ /P₂ O₅ compound in which the ratio of R₂ O₃ to P₂ O₅ is 1 to 3 and R is La, Y, Ce, Nd, Eu, Pt, Sm, Ho, Tb, Er, Yb, Tm or Dy. The invention also relates to a method of making the diffusion source, a method of using the diffusion source to evolve P₂ O₅ to dope a silicon wafer, and to the doped silicon wafer.

BACKGROUND OF THE INVENTION

A solid diffusion source comprising glass ceramic or polycrystalline particles is disclosed in the Rapp U.S. Pat. No. 4,141,738. In U.S. Pat. No. 4,033,790 there is disclosed solid diffusion sources made by hot pressing R₂ O₃ /P₂ O₅ (La₂ O₃ /P₂ O₅, Ce₂ O₃ /P₂ O₅ and Y₂ O₃ /P₂ O₅) compounds in which the R₂ O₃ to P₂ O₅ is mainly 1 to 5. The above U.S. patents are incorporated by reference.

U.S. Pat. No. 4,846,902 discloses a solid diffusion source that is a Gd oxide/P₂ O₅ compound in which the ratio of Gd oxide to P₂ O₅ to about 1/1 to 1/5.

It is desirable to provide a solid diffusion source that is easily and efficiently made, and a source that evolves P₂ O₅ relatively rapidly at a relatively high temperature.

OBJECTS OF THE INVENTION

It is an object of the present invention to prepare a doping composition as a diffusion source to provide a doped silicon wafer, the composition being a meta phosphate R₂ O₃ /P₂ O₅ in which the ratio of R₂ O₃ to P₂ O₅ is 1 to 3 and R is La, Y, Ce, Nd, Eu, Pr, Sm, Ho, Tb, Er, Yb, Tm or Dy.

It is an object of the present invention to provide a method of making a doped silicon wafer using a solid diffusion source, the method comprising the steps of:

A. heating R₂ O₃ oxide and H₃ PO₄ to provide a R₂ O₃ oxide/P₂ O₅ composition consisting essentially of a R₂ O₃ /P₂ O₅ compound in which the ratio of R₂ O₃ to P₂ O₅ is 1 to 3 and R is La, Y, Ce, Nd, Eu, Pt, Sm, Ho, Tb, Er, Tm, Yb or Dy.

B. firing the composition to evolve P₂ O₅ to deposit a phosphorus containing coating on the silicon wafer at a relatively high temperature and at a relatively high rate to form a glassy layer on the silicon wafer.

These and other objects will be apparent from the specification that follows and the appended claims.

SUMMARY OF THE INVENTION

The present invention provides a composition for a solid diffusion source to deposit a phosphorus oxide coating on a silicon wafer, the composition consisting essentially of an R₂ O₃ /P₂ O₅ compound in which the ratio of R₂ O₃ to P₂ O₅ is about 1 to 3, and R is La, Y, Ce, Nd, Eu, Pr, Sm, Ho, Tb, Er, Yb, Tm or Dy. The present invention also provides the R₂ O₃ ·3P₂ O₅ compound in which it contains SrO₂.

The present invention also includes a method of using the doping source by firing it at about 950° C. up to about 1165° or 1200° C. and the doped silicon wafer itself.

The present invention also provides a method of making and using the doping source at a temperature preferably at about 975° C. to 1125° C. or above.

The present invention also provides a doping composition in which the above described meta phosphate doping compound contains ZrO₂.

DETAILED DESCRIPTION OF THE INVENTION

In the present invention, R is Group IIIa element (according to the Periodic Chart of the Elements, Page 46 of the International Critisol Tables of Numerical Data, Physics, Chemistry and Technology, 1926, McGraw-Hill). The suitable group IIIa elements have atomic numbers from 37-70 but not 64.

In one aspect, the R element has an atomic number from 39-57 (Y and La) or 58-63 (Ce, Pr, Nd, Sm and Eu). Suitable R elements also have an atomic number from 65-70 (Tb, Dy, Ho, Er, Tm and Yb).

Y is a preferred R element as are La, Yb, Ce, Dy, Er and Sm--these compounds being colorless or white or near white. Y is highly preferred in some applications, it evolving P₂ O₅ at a high rate at about 950° C. or 1000° C. to 1165° or 1175° C., it being fired preferably at least about 1000° C. and optimally at about 1050° to 1150° C. to provide a glassy film of about 800-1000 A° on a silicon wafer in one hour.

EXAMPLE 1

Various R₂ O₃ ·3P₂ O₅ sources were prepared using stoichiometric amounts of R₂ O₃ and P₂ O₅ (in the H₃ PO₄ starting material) as described in the Pickrell U.S. Pat. No. 4,846,902 for Gd₂ O₃ ·5P₂ O₅ materials and in U.S. Pat. No. 4,033,790 for R₂ O₃ ·5P₂ O₅ materials.

In each case, the R₂ O₃ was mixed with an appropriate stoichiometric amount of H₃ PO. The excess water is evaporated, and the mixed product fired at 750° C. for 15 hours to provide the R₂ O₃ ·3P₂ O₅ product.

The fired material was pressed and sintered as in the U.S. Pat. No. 4,033,790, the resultant billet being sliced into individual diffusion source wafers.

In a typical formulation, the following was mixed in approximate grams to provide the following approximate stoichiometric amounts of 1 mole R₂ O₃ and 3 moles P₂ O₅ mixture:

    ______________________________________                                         Ingredients      Grams                                                         ______________________________________                                         Lanthanum Oxide  107                                                           1 mole (La.sub.2 O.sub.3)                                                      to 3 moles (P.sub.2 O.sub.5)                                                   H.sub.3 PO.sub.4 (85%)                                                                          230                                                           ______________________________________                                    

The procedure followed is set forth in the aforementioned Pickrell U.S. Pat. No. 4,846,902, the water of the R₂ O₃ /P₂ O₅ mixture being driven off the mixture by heating at 150° C. Thereafter, the crucible was covered and fired at 750° C. for 15 hours to provide the lanthanum oxide/3P₂ O₅ product. The resultant crystalline product was ball-milled to obtain a fine powder (-60 mesh).

Silicon wafer and the metaphosphate source made from the sintered powder were heated to 1075° C. and the metaphosphate source fired at 1075° C. for 1 hour to evolve P₂ O₃ and coat the heated wafers with a glassy film of about 1000A° in thickness. This is a sufficient amount of glass to satisfactorily dope the silicon wafers with phosphorus at 1075° C. Excellent film thickness also was obtained by firing for 1 hour at 975° C. to 1125° C. and as high as 1165° C.

Other doping source R₂ O₃ ·3P₂ O₅ compounds were prepared and fired for 1 hour to evolve P₂ O₅ at the temperature indicated in the table below to coat silicon wafers with a glassy film of about 500-2500A°.

    ______________________________________                                         R.sub.2 O.sub.3.3P.sub.2 O.sub.5 Compound                                                         Firing Temperature °C.                               ______________________________________                                         La.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                  975-1165                                                   Y.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                   975-1165                                                   Pr.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                 1025-1125 or 1165                                           Nd.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                 1000-1125 or 1165                                           Sm.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                 1075-1165                                                   Dy.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                 1000-1075 or 1165                                           Er.sub.2 O.sub.3.3P.sub.2 O.sub.5                                                                  950-1165                                                   La.sub.2 O.sub.3.ZrO.sub.2.3P.sub.2 O.sub.5                                                        975-1125 or 1165                                           ______________________________________                                    

As in the case of La₂ O₃ ·ZrO₂ ·3P₂ O₅, substantially similar results can be obtained by the use of ZrO₂ in the other rare earth oxide/·3P₂ O₅ compounds.

In the R₂ O₃ ·3P₂ O₅ compounds, R is a Group IIIa rare earth element (International Critical Tables) having an atomic number as follows:

    ______________________________________                                         R             Atomic Number                                                    ______________________________________                                         Y (or Yt)     39                                                               La            57                                                               Ce            58                                                               Pr            59                                                               Nd            60                                                               Sm            62                                                               Eu            63                                                               Tb            65                                                               Dy            66                                                               Ho            67                                                               Er            68                                                               Tm (or Tu)    69                                                               Yb            70                                                               ______________________________________                                    

The preferred R elements are Group IIIa elements Y and La, having atomic numbers of 39-57, respectively. Also preferred for some applications are Yb, Ce, Dy, Er and Sm, the resultant compounds being colorless or white or near white.

Good results are obtained when the Group IIIa element has an atomic number of from 58 to 63 or from 65 to 70.

The above examples illustrate the R₂ O₃ ·3P₂ O₅ diffusion sources, the methods of making the diffusion sources, the methods of using the sources by firing the same to evolve P₂ O₅, and methods of making the doped silicon wafers that are useful in a typical emitter diffusion, in channel MOS diffusion and in doping of a polysilicon layer without undesirable toxic gases and liquids.

Lanthanum Pentaphosphate was held at 1000° C. to convert it to Lanthanum Metaphosphaste, after losing about 26% of its weight. The source was used to dope silicon at 1100° C. for 1 hour. A glassy layer of 1000A° was deposited on the silicon and it had a sheet resistivity of 2.65 ohm/square (Ω/□) .

The metaphosphates of Dy, Gd, Er and Y were prepared and ground into fine powders for screen printing on silicon. Doping tests at 1100° C. and 1150° C. indicated that ErP3 (erbium oxide/3P₂ O₅), YP3 and ErP5 can be used as sources at temperature as high as 1100° C.

A sample of lanthanum zirconium phostphate (meta) was prepared, made into a fine powder and deposited on a silicon wafer. After firing at 1200° C. for 1 hour, the residual material etched away in HF in 1 hour. The silicon exhibited a gold-brown color and had a sheet resistivity of 0.4 ohm/square (Ω/□). It was used as a satisfactory deep junction diode. 

What is claimed is:
 1. A composition for a solid diffusion source to deposit a phosphorus oxide coating on a silicon wafer, the composition consisting essentially of an R₂ O₃ /P₂ O₅ compound in which the ratio of R₂ O₃ to P₂ O₅ is about 1:3, and R is La, Y, Ce, Nd, Eu, Pr, Sm, Ho, Tb, Er, Yb, Tm or Dy.
 2. A composition as defined in claim 1 in which R is La or Y.
 3. A composition as defined in claim 1 in which R is Ce.
 4. A composition as defined in claim 1 in which R is Nd, Eu, Pr or Sm.
 5. A composition as defined in claim 1 in which R is Sm, Ho, Tb, Er, Yb, Tm or Dy.
 6. A composition as defined in claim 1 in which R is Er.
 7. A composition as defined in claim 1 in which R is Sm.
 8. A composition as defined in claim 1 in which the R₂ O₃ /P₂ O₅ compound contains ZrO₂.
 9. A composition as defined in claim 1 in which the compound is Ce₂ O₃ ·3P₂ O₅. 